PA66 德国巴斯夫 8202HS 注塑级 

特性	热稳定;高抗冲
应用领域	电气应用;工业机械

收缩率	MD：3.18mm		1.2	%
吸水率	24hr	ASTMD570	1.6	%
	23°C,24hr	ISO62	1.6	%
	饱和	ASTMD570	9.5	%
	饱和,23°C	ISO62	9.5	%
	平衡,50%RH	ASTMD570	2.7	%
	平衡,23°C,50%RH	ISO62	2.7	%
机械性能	测试条件	测试方法	测试结果	单位
标称拉伸断裂应变	23°C	ISO527-2	25	%
抗张强度	断裂,23°C	ASTMD638	75.0	Mpa
	屈服,-40°C	ASTMD638	126	Mpa
	屈服,23°C	ASTMD638	79.0	Mpa
	屈服,80°C	ASTMD638	35.0	Mpa
	Yield,121°C	ASTMD638	25.0	Mpa
拉伸模量	23°C	ISO527-2	2700	Mpa
	80°C	ISO527-2	485	Mpa
	120°C	ISO527-2	360	Mpa
	150°C	ISO527-2	290	Mpa
拉伸应变	屈服,23°C	ISO527-2	4.0	%
拉伸应力	屈服,120°C	ISO527-2	25.0	Mpa
	屈服,150°C	ISO527-2	20.0	Mpa
	屈服,-40°C	ISO527-2	126	Mpa
	屈服,23°C	ISO527-2	78.0	Mpa
	屈服,80°C	ISO527-2	35.0	Mpa
伸长率	断裂,23°C	ASTMD638	55	%
	屈服,23°C	ASTMD638	4.0	%
	屈服,80°C	ASTMD638	42	%
	Yield,121°C	ASTMD638	36	%
弯曲模量	-40°C	ASTMD790	3010	Mpa
	23°C	ASTMD790	2830	Mpa
	65°C	ASTMD790	500	Mpa
	90°C	ASTMD790	350	Mpa
	121°C	ASTMD790	305	Mpa
	23°C	ISO178	2400	Mpa
弯曲强度	-40°C	ASTMD790	170	Mpa
	23°C	ASTMD790	108	Mpa
	65°C	ASTMD790	30.0	Mpa
	90°C	ASTMD790	20.0	Mpa
	121°C	ASTMD790	17.0	Mpa
弯曲应力	23°C	ISO178	85.0	Mpa
热性能	测试条件	测试方法	测试结果	单位
RTIElec	0.71mm	UL746	130	°C
	1.5mm	UL746	130	°C
	3.0mm	UL746	130	°C
	6.0mm	UL746	130	°C
RTIImp	0.71mm	UL746	95.0	°C
	1.5mm	UL746	105	°C
	3.0mm	UL746	105	°C
	6.0mm	UL746	105	°C
RTIStr	0.71mm	UL746	95.0	°C
	1.5mm	UL746	105	°C
	3.0mm	UL746	105	°C
	6.0mm	UL746	105	°C
热变形温度	0.45MPa,未退火	ASTMD648	178	°C
	0.45MPa,未退火	ISO75-2/B	150	°C
	1.8MPa,未退火	ASTMD648	65.0	°C
	1.8MPa,未退火	ISO75-2/A	60.0	°C